Introduction:
Cracked Low-Density Polyethylene Wax | KIAWax-CR110 is a high-performance viscosity polyethylene wax obtained from virgin LDPE by thermal cracking method.
Industry:
- Polymer Compounding Industry
- Hot-Melt Adhesive Industry
- Rubber Industry
Application:
Polyolefin compounds and masterbatches - Wood plastics composites - Hot-melt adhesives - Rubber compounding
* Non-polar polyethylene wax with a higher melting point
* Acts as a lubricant, release agent, and dispersing agent
* Good thermostability and anti-sticking properties
| Color | White |
| Appearance | Powder | on customer request |
| Method of production | Thermal cracking |
| Packaging | 25 kg bags |
Product properties will change minimally under the following storage conditions:
| * Ambient temperature (25-35 °C) | * Away from fire |
| * Dry place | * on the pallet |
| Test | Method | Specification | |
|---|---|---|---|
| Value | Units | ||
| Viscosity @140°C | ASTM D3236 | 650 ±50 | cp |
| Viscosity @120°C | ASTM D3236 | 1,600 ±100 | cp |
| Softening Point | ASTM D-2398 | 110 ±3 | °C |
| Acide Value | - | 0 | mg KOH/gr |
| Density @25°C | ASTM D792 | 0.91 ±0.01 | gr/cm3 |